Product classification
  • Rainbow Hot Stamping Foil Film
  • Rainbow Hot Stamping Foil Film

    It is a special type of foil film used in packaging that features a spectrum of colors, creating a unique and eye-catching visual effect when heated and stamped onto a surface.


    • ¥0.00
      ¥0.00
Product Description

It is a special type of foil film used in packaging that features a spectrum of colors, creating a unique and eye-catching visual effect when heated and stamped onto a surface.



Application


This product is suitable for high-end cigarette or special high-end brand packaging.



Key Features


  • High gloss, enhancing the visual effect of the printing film

  • Excellent slip performance, suitable for high-speed packaging

  • Outstanding wear resistance

  • Cold stamping process ensures film size stability

  • Excellent heat resistance

  • It is a semi-transparent material, allowing the packaged item to be visible




Technical Data

Properties

Unit

Typical Values

Test Standards

Company  standard

National 

Standard

International 

Standard

Density

g/cm³

0.94



ASTM D1505

Thickness

μm

21

Q/SN2

GB/T6672-86


Unit Weight

g/㎡

19.74




Tensile Strength

MD

N/m㎡

180

Q/SN2

GB/T1040-92

ASTM D882

TD

296

Thermal shrinkage

MD

%

8

Q/SN2

GB/T12026-89

ASTM D1204-89

TD

8

Elongation at break

MD

%

170

Q/SN2

GB/T1040-92

ASTM D882

TD

55

Young’s modulus

MD

N/m㎡

2650

Q/SN2


ASTM D882

TD

Heat seal strength

TD

N/15mm

3.5

Q/SN2

ZBY28004

ASTM F88-94

Heat seal temperature range

120~150

Q/SN2

ZBY28004

ASTM F88-94

Friction coefficient (film/film)


0.15

Q/SN2

GB/T10006-88

ASTMD1894-93

Haze

%

1.2

Q/SN2

GB2410-80

ASTMD1003-95

Gloss(45°)

%

93

Q/SN2

GB8807-88

ASTM D2457

Water vapor transmission rate

 g/㎡·24hr

4.0


GB8807-88

ASTM F1249-90  23℃ 85%RH



Note: 

The performance indicators in the table are typical values and not guaranteed values.

They are for reference only.

The specific indicators should be subject to the contract.